1. Stir the base (Part A) well before use (except when machine dispensing).
  2. Shake the catalyst container (Part B) well before use.
  3. Weigh the desired amount of base into a clean mixing container. Tip the container and roll the base all the way 
    around the side wall up to two inches from the top. This will prevent the catalyst from becoming absorbed into the 
    container. It is recommended that the container be filled to not more than 1/3 the container depth to allow sufficient
  4. room for expansion during the deaeration procedure.
  5. Weigh the proper amount of catalyst into the container. Mix the base and catalyst together by stirring with a stiff, flat ended metal spatula until a uniform color is obtained. Scrape the container walls and bottom well to insure a thorough mix.
  6. Place the container into a vacuum chamber and evacuate the entrapped air from the mixture using a vacuum pump capable of achieving 29 inches of mercury vacuum. The mixture will rise, crest and then collapse in the container. Interruption (bumping) of the vacuum may be necessary to prevent overflowing the container. Keep the mixture under full vacuum for 2-3 minutes after the material has receded in the container.
  7. Bleed air slowly into the vacuum chamber. When the chamber is at atmospheric equilibrium, remove the cover 
    plate and take out the container.
  8. Pour the deaired material slowly in a steady stream from one end of the mold box so that the material flows evenly over the pattern.  This should minimize entrapment of air bubbles under the flowing material. A "print" coat may be poured first over the pattern which will also help reduce the possibility of entrapping air on the pattern and in the cured rubber. A mold release (petroleum jelly) may be applied on the pattern first to improve release.
  9. Allow the rubber to cure for 16-24 hours at 75±5°F (24°C) before removing the cured rubber mold from the pattern. 
    Heat acceleration is not recommended with this product.
  10. For best results, allow the mold to air cure an additional 24 hours before using it in production.  Full cure is achieved in 3-7 days.
  11. For bonding to wood or metals, use BLUESIL V-04 primer.  Follow recommendations on the BLUESIL V-04 technical data sheet for best results.

                           PROCESSING INFORMATION


  1. For best results, mix and cure the material at 75°F (24°C) and 50% relative humidity.
  2. Higher temperature and humidity will decrease the work life and pot life of the material. The faster cure will also affect the flow properties. Refrigeration of the base prior to use in hot environments has shown to improve the handling properties of this material.
  3. Lower temperatures and humidity will increase the work life and pot life of the material. The slower cure will increase the flow time. Cure temperatures below 68°F (20°C) are not recommended and have been found to cause a reduction in final cure hardness and properties.
  4. It is important that the catalyst containers are tightly closed after use. Catalyst exposed to air for extended periods of time will hydrolyze (cure). An indication of hydrolysis is a film or crust formation on the surface of the catalyst. The use of hydrolyzed catalyst is not recommended and may cause incomplete cure.

请保存在原装密闭容器中 BLUESIL V-1022 B 的标准有效期是从生产日期起 24个月 请参考包装上的储存建议和失效日期。超期后,埃肯有机硅将不再保证产品符合销售规范。



BLUESIL V-1022 is a medium hardness, self-bonding, room temperature curing silicone rubber compound. It is designed as a potting and encapsulating material for environmental and dielectric protection of electrical, electronic and mechanical parts and assemblies.

BLUESIL V-1022 is a primerless-bonding, thick section curing rubber, which will bond to most metals and many plastics.



​• Potting and encapsulating of electrical and electronic device           

• Bonding and sealing electronic and mechanical parts and assemblies

















BLUESIL V-1022 ABLUESIL V-1022 A/our_offer/Product/90035921/90035922/BLUESIL-V-1022-A