1. Mixing the two components
The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or by using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase.
It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.

2. Degassing
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.
The silicone mixture expands to times of its initial volume and bubbles rise to the surface. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.

3. Polymerisation
The system polymerises at . The curing may be slowed down at lower temperature or accelerated by heat.
Contact with certain materials can inhibit the crosslinking. See list below:

• Natural rubbers vulcanised with sulphur.
• RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds.
• PVC stabilised with tin salts and additives.
• Epoxy resins catalysed with amines.

SILBIONE RT GEL 4320 FC A

SILBIONE RT GEL 4320 FC A&B is a two component silicone elastomer which cures at room temperature by a polyaddition reaction. The polymerisation can be accelerated by heat.
The silicone material is delivered as two low viscous liquid components, which once mixed and cured, transform into an elastic gel. Polymerisation occurs without formation of heat.

粘附力;生物相容性

双组份室温硅橡胶

凝胶

医疗设备一类;皮肤接触

• Very good adhesion on dry skin.
• No adhesion on moist wounds.
• Proven biocompatibility.
• No free oil.

• Adhesive wound dressings.
• Adhesive sheets for scar treatment.

亚太区;欧洲中东非洲;中南美;北美